Addendo Mg, P et alia elementa vestigialia ad matricem cupri, C18665 praebet magnam vim, elasticitatem, excellentem conductivitatem, resistentiam relaxationis stress et resistere corrosioni per stress. C18665 potest uti ad conficienda materia quaevehicularia terminales, relais mobilis contactus, virentes contactus, busbars, circuit breaker, terminales batteriarum, fuses etc.
| Gradus | Compositio chimica (% ) ≤ | Crassitudo (mm) |
||||
| EN | GB | ASTM | Cu | MG | P | |
| CuMgP | TMg0.5 | C18665 | ≥99.0 | 0.4-0.9 | 0.002-0.04 | 0.08-5.0 |
| Proprietates physicae | |||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
|||
| 8.8 | 125 | 17.3 | 60 | 253 | |||
| Proprietates mechanicæ | Flexurae proprietates | |||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R\/T(Crassus＜0.5mm) | |||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Mala via | ||
| H01 | 90-140 | 365-450 | 300-410 | ≥15 | 0 | 0 |
| H02 | 120-170 | 420-510 | 370-480 | ≥10 | 0 | 0 |
| H04 | 150-190 | 480-570 | 440-550 | ≥7 | 0 | 0.5 |
| H06 | 170-210 | 540-630 | 490-620 | ≥5 | 0 | 1 |
| H08 | ≥180 | ≥590 | ≥540 | - | - | - |
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci in stock sunt. Aut minus quam 30 dies, si merci non sunt in stock, iuxta quantitatem.
Q: Praebitisne exempla?
A: Ita, possumus praebere exemplar
Q: Quae sunt tua termini solvendi
A: 30% T/T ante, reliquum ante navationem. Et pretium dependet a materia et quantitate
Si habes alteram quaestionem, noli hesitare nobiscum conari.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN