Addendo Mg, P et alias elementa vestigialia ad matricem cupri, confertur C18665 magna fortitudo, elasticitas, optima conductio, resistencia relaxationis stress, et resistencia corruptionis stress. C18665 potest ad fabricandum materiales ut terminales automotivae, contactus mobilis relais, virectrices spring, busbars, circuitus interruptores, terminales batteriarum, fuses etc. adhiberi.
| Gradus | Compositio chemica (% ) ≤ | Crassitudo (mm) |
||||
| EN | GB | ASTM | Cu | MG | P | |
| CuMgP | TMg0.5 | C18665 | ≥99.0 | 0.4-0.9 | 0.002-0.04 | 0.08-5.0 |
| Proprietates physicae | |||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
|||
| 8.8 | 125 | 17.3 | 60 | 253 | |||
| Proprietates mechanicæ | Proprietates curvandi | |||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R\/T (Crassus＜0.5mm) | |||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Via mala | ||
| H01 | 90-140 | 365-450 | 300-410 | ≥15 | 0 | 0 |
| H02 | 120-170 | 420-510 | 370-480 | ≥10 | 0 | 0 |
| H04 | 150-190 | 480-570 | 440-550 | ≥7 | 0 | 0.5 |
| H06 | 170-210 | 540-630 | 490-620 | ≥5 | 0 | 1 |
| H08 | ≥180 | ≥590 | ≥540 | - | - | - |
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci sunt in stock. Aut infra 30 dies, si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, possumus praebere exemplar
Q: Quae sunt tua termini solvendi
A: 30% T/T ante propter praestationem, reliquum ante navationem. Et pretium dependet a materia et quantitate
Si habes alteram quaestionem, noli hesitare nobiscum conari.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN