Est latissime usum in parvis conectoribus, contactibus springis, relay springis, terminis, partibus commutationis, fusilibus tenaculis, et electronicis conectoribus.
| Gradus | Compositio chymica (%)) | Crassitudo (mm) |
|||||
| GB | ASTM | JIS | Cu | Stannum | P | Fe | 0.2-2.0 |
| - | C50715 | - | RESPONDEO | 1.7-2.3 | 0.025-0.04 | 0.05-0.15 | |
| Proprietates physicae | |||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
|||
| 8.9 | 121 | 17.6 | 32 | 160 | |||
| Proprietates mechanicæ | Proprietates curvandi | ||||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R\/T (Crassitudo < 0.8mm) | ||||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Via mala | |||
| H02 | 120-165 | 395-500 | 295-415 | ≥16 | 0 | 0 | |
| H04 | 160-190 | 515-600 | 440-545 | ≥6 | 0 | 1 | |
| H06 | 170-200 | 550-625 | 490-570 | ≥5 | 0.5 | 1.5 | |
| H08 | ≥185 | 605-665 | 550-625 | ≥3 | - | - | |
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci sunt in stock. Aut infra 30 dies, si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, possumus praebere exemplar
Q: Quae sunt tua termini solvendi
A: 30% T/T ante propter praestationem, reliquum ante navationem. Et pretium dependet a materia et quantitate
Si habes alteram quaestionem, noli hesitare nobiscum conari.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN