C51000 Phosphoricus Aes introducio
C51000 est aes phosphori cum stanno, cuius contentus stanni est circiter 5.0%. Hoc conglutinatum habet altam elasticitatem, vim, resistendo frictui, resistentiam altiori calori, resistendo relaxationi stressis, et resistendo corruptioni. Posset ad fabricandum usus novae vehiculi energetici connectores, terminales filorum, partes pressiles, conectores elasticos etc.
| Gradus | Compositio chymica (%)) | |||||||
| GB | ASTM | DIN | Cu | Fe | Pb | Stannum | P | Zn |
| Qsn5-0.2 | C51000 | CuSn5 | RESPONDEO | ＜0.1 | ＜0.05 | 4.2-5.8 | 0.03-0.35 | ＜0.3 |
| Proprietates physicae | ||||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity (W∕(m·K)) |
||||
| 8.86 | 115 | 17.2 | 17 | 81 | ||||
| Proprietates mechanicæ | Proprietates curvandi | |||||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R\/T（Crassitudo≤0.5mm） | |||||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Via mala | ||||
| O60 | 80-120 | ≥305 | - | ≥45 | 0 | 0 | ||
| H01 | 90-160 | 370-470 | - | ≥30 | 0 | 0.5 | ||
| H02 | 130-190 | 470-570 | 400-500 | ≥18 | 0.5 | 1 | ||
| H04 | 170-220 | 570-665 | 500-630 | ≥10 | 1 | 2 | ||
| H06 | 190-230 | 620-710 | 570-680 | ≥7 | 1 | 3 | ||
| H08 | ≥200 | ≥660 | ≥630 | ≥5 | - | - | ||