Introducio C51100 Aerei Phosphori
C51100 est aes stannum phosphoricum cum contentione Sn fere 4.0%. Hoc conglutinatum habet altam elasticitatem, vim, resistendo attriti, altitudinem patientiam, resistentiam relaxationis stress, et corrosionis resisteam. Id fieri potest ad conficiendum connectores vehiculorum novae energiae, terminales filiorum, partes formandae, connectores elasticos etc.
| Gradus | Compositio chymica (%)) | ||||||||
| GB | ASTM | JIS | DIN | Cu | Fe | Pb | Stannum | P | Zn |
| Qsn4.0-3.0 | C51100 | C5111 | CuSn4 | RESPONDEO | ＜0.1 | ＜0.05 | 3.5-4.9 | 0.03-0.35 | ＜0.3 |
| Proprietates physicae | |||||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10 -6\/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity (W∕(m·K)) |
|||||
| 8.86 | 115 | 17.2 | 20 | 83 | |||||
| Proprietates mechanicæ | Proprietates curvandi | ||||||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 180°R\/T (Crassus) ≤ 0.5mm） | ||||||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Via mala | |||||
| O60 | 75-120 | ≥ 295 | - | ≥ 45 | 0 | 0 | |||
| H01 | 80-150 | 345-440 | - | ≥30 | 0 | 0.5 | |||
| H02 | 120-180 | 410-510 | 340-460 | ≥17 | 0.5 | 1 | |||
| H04 | 150-200 | 490-590 | 420-560 | ≥12 | - | 2 | |||
| H06 | 170-220 | 570-660 | 500-630 | ≥6 | - | - | |||
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci sunt in stock. Aut infra 30 dies, si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, exemplum praebere possumus.
Q: Quae sunt tua condiciona praepositionis?
A: 30% T/T ante, reliquum ante navationem. Et pretium dependet a materia et quantitate.
Si habes alteram quaestionem, noli hesitare nobiscum conari.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN