Introducio aerei phosphorati C52100
Perfusio: Praestans ductilitas, resistencia ad fatigationem, et resistencia ad corruptionem
Est late usus in productione variorum contactuum helicum, electronicorum contactuum, pennae frictrices, et commutator partium etc
Ad utendum in producendo productis laminae phosphori cupri finis granuli, cum magnitudine granuli ≤ 0.005mm
Nunc, C52100 (C5210/QSn8-0.3) est secunda in productione copiosa productorum galvanicorum (electrotypia physica) cum stratis stannae 1-6μm quae sunt acceptabiles.
| Standardus | Gradus | Compositio chimica（%） ≤ | ||||||||||||||||
| Stannum | Zn | Fe | Pb | Ni | P | Other | Cu | |||||||||||
| GB | QSn8-0.3 | 7.0-9.0 | 0.20 | 0.10 | 0.05 | - | 0.03-0.35 | 0.5 | RESPONDEO | |||||||||
| EN | CuSn8 | 7.5-8.5 | 0.20 | 0.10 | 0.02 | 0.2 | 0.01-0.4 | 0.2 | RESPONDEO | |||||||||
| ASTM | C52100 | 7.0-9.0 | 0.20 | 0.10 | 0.05 | - | 0.03-0.35 | - | RESPONDEO | |||||||||
| JIS | C5210 | 7.0-9.0 | 0.20 | 0.10 | 0.02 | - | 0.03-0.35 | 0.5 | RESPONDEO | |||||||||
| Proprietates physicae | ||||||||||||||||||
|
Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
||||||||||||||
| 8.8 | 110 | 18.5 | 11 | 67 | ||||||||||||||
| Proprietates mechanicæ | ||||||||||||||||||
| Gradus | status |
Robur Tensile Rm\/MPa |
Tentio A11.3/% |
Dureza HV |
||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | EN |
GB (HV) |
JIS (HV) |
ASTM (HR) |
EN (HV) |
| QSn8-0.3 | C5210 | C52100 | CuSn8 | O60 | O60 | R370/H090 | ≥345 | 365-460 | 370-450 | ≥45 | ≥50 | ≤120 | 20-70 | 90-120 | ||||
| H01 | R450/H135 | 390-510 | - | 450-550 | ≥40 | ≥20 | 100-160 | - | 135-175 | |||||||||
| H02 | 1/2H | H02 | R540/H170 | 490-610 | 470-610 | 475-580 | 540-630 | ≥30 | ≥27 | ≥13 | 150-205 | 140-205 | 69-91 | 170-200 | ||||
| H04 | H | H04 | R600/H190 | 590-705 | 590-705 | 585-690 | 600-690 | ≥12 | ≥20 | ≥50 | 180-235 | 185-235 | 89-97 | 190-220 | ||||
| H06 | EH | H06 | R660/H210 | 685-785 | 685-785 | 670-770 | 660-750 | ≥5 | ≥11 | ≥3 | 210-250 | 210-260 | 93-100 | 210-240 | ||||
| H08 | Sh | H08 | R740/H230 | ≥735 | 735-835 | 725-820 | ≥740 | - | ≥9 | ≥2 | ≥230 | 230-270 | 95-102 | ≥230 | ||||
| - | ESH | H10 | - | - | 770-885 | 760-830 | - | - | ≥5 | - | - | 245-285 | 96-103 | - | ||||
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci sunt in stock. Aut infra 30 dies, si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, possumus praebere exemplar
Q: Quae sunt tuae conditiones praepositionis?
A: 30% T/T ante, reliquum ante navationem. Et pretium dependet a materia et quantitate.
Si habes alteram quaestionem, noli hesitare nobiscum conari.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN