Introducio aerei phosphorati C52100
Perfusio: Praestans ductilitas, resistencia ad fatigationem, et resistencia ad corruptionem
Est late usata in productione variorum contactuum helicoidum, contactuum electronicorum, penarum filamentarum, et partium commutationis etc. Potest uti ad producendum producta laminae phosphori cupri cum grano tenuissimo, cum magnitudine grani ≤ 0.005mm. Nunc, C52100 (C5210/QSn8-0.3) est secunda in productione copiosa productorum galvanicorum (electrotypia physica) cum stratis stannae 1-6μm quae sunt acceptabiles.
| Standardus | Gradus | Compositio chimica（%） ≤ | ||||||||||||||||
| Stannum | Zn | Fe | Pb | Ni | P | Other | Cu | |||||||||||
| GB | QSn8-0.3 | 7.0-9.0 | 0.20 | 0.10 | 0.05 | - | 0.03-0.35 | 0.5 | RESPONDEO | |||||||||
| EN | CuSn8 | 7.5-8.5 | 0.20 | 0.10 | 0.02 | 0.2 | 0.01-0.4 | 0.2 | RESPONDEO | |||||||||
| ASTM | C52100 | 7.0-9.0 | 0.20 | 0.10 | 0.05 | - | 0.03-0.35 | - | RESPONDEO | |||||||||
| JIS | C5210 | 7.0-9.0 | 0.20 | 0.10 | 0.02 | - | 0.03-0.35 | 0.5 | RESPONDEO | |||||||||
| Proprietates physicae | ||||||||||||||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10 -6\/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
||||||||||||||
| 8.8 | 110 | 18.5 | 11 | 67 | ||||||||||||||
| Proprietates mechanicæ | ||||||||||||||||||
| Gradus | status | Robur Tensile Rm\/MPa |
Tentio A11.3/% |
Dureza HV |
||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | EN | GB (HV) |
JIS (HV) |
ASTM (HR) |
EN (HV) |
| QSn8-0.3 | C5210 | C52100 | CuSn8 | O60 | O60 | R370/H090 | ≥345 | 365-460 | 370-450 | ≥45 | ≥50 | ≤120 | 20-70 | 90-120 | ||||
| H01 | R450/H135 | 390-510 | - | 450-550 | ≥40 | ≥20 | 100-160 | - | 135-175 | |||||||||
| H02 | 1/2H | H02 | R540/H170 | 490-610 | 470-610 | 475-580 | 540-630 | ≥30 | ≥27 | ≥13 | 150-205 | 140-205 | 69-91 | 170-200 | ||||
| H04 | H | H04 | R600/H190 | 590-705 | 590-705 | 585-690 | 600-690 | ≥12 | ≥20 | ≥50 | 180-235 | 185-235 | 89-97 | 190-220 | ||||
| H06 | EH | H06 | R660/H210 | 685-785 | 685-785 | 670-770 | 660-750 | ≥5 | ≥11 | ≥3 | 210-250 | 210-260 | 93-100 | 210-240 | ||||
| H08 | Sh | H08 | R740/H230 | ≥735 | 735-835 | 725-820 | ≥740 | - | ≥9 | ≥2 | ≥230 | 230-270 | 95-102 | ≥230 | ||||
| - | ESH | H10 | - | - | 770-885 | 760-830 | - | - | ≥5 | - | - | 245-285 | 96-103 | - | ||||
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci sunt in stock. Aut infra 30 dies, si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, possumus praebere exemplar
Q: Quae sunt tua termini solvendi
A: 30% T/T ante propter praestationem, reliquum ante navationem. Et pretium dependet a materia et quantitate
Si habes alteram quaestionem, noli hesitare nobiscum conari.