Introducio aerei phosphorati C52400
C52400 est ligamentum cupri phosphori cum stanno in proportione fere 10%. Habet proprietates alti elastici, firmitatis magnae, resistendo corrosioni et attritioni, fatigationi, anti magnetismo, facile brazando, et bono operationis performatu.
Usus est late in communicatione, apparatu electrico, instrumentis, et industria mechanica, et communiter ad fabricandum partes elasticas ut terminales conectorum, contactores, contactus, et conectorum.
| Standardus | Gradus | Compositio chymica (%)) | |||||
| Stannum | Zn | Fe | Pb | P | Cu | ||
| ASTM | C52400 | 9.0-11.0 | ＜0.2 | ＜0.1 | ＜0.05 | 0.03-0.35 | RESPONDEO |
| JIS | C5240 | 9.0-11.0 | ＜0.2 | ＜0.1 | ＜0.2 | 0.03-0.35 | - |
| Proprietates physicae | |||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10 -6\/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
|||
| 8.86 | 110 | 18.4 | 10 | 50 | |||
| Proprietates mechanicæ | Proprietates curvandi | ||||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R\/T (Crassus ≤ 0.5mm） | ||||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Via mala | |||
| H04 | 200-240 | 650-750 | 510-700 | ≥15 | 0 | 0.5 | |
| H06 | 230-270 | 750-850 | 630-800 | ≥12 | - | 1.5 | |
| H08 | 250-300 | 850-950 | 750-910 | ≥5 | - | 2.5 | |
| H10 | ≥270 | ≥950 | 870-1010 | ≥1 | - | - | |
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci sunt in stock. Aut infra 30 dies, si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, exemplum praebere possumus.
Q: Quae sunt tua condiciona praepositionis?
A: 30% T/T ante, reliquum ante navationem. Et pretium dependet a materia et quantitate.
Si habes alteram quaestionem, noli hesitare nobiscum conari.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN