CuCrAgFeTiSi alloy est alloy aeneum cum alta conductivitate et precipitatione senectutis fortificante, quod combinat altam conductivitatem et thermicam conductivitatem. Habet etiam unicum et praestantem calidum et frigidum operationem, altam resistendam attritionem, altam electroplating performance, resistendo relaxationi stressis altis temperaturebus et ablationi electrode. In recentibus annis, paulatim applicatur in connectores sicut automotive power assemblies et potentia batteriarum charge.
| Gradus | Compositio chemica (% ) ≤ | |||||
| Norma enterprise | Cu | Cr | Ag | Fe | Ti | Si |
| CY88 | RESPONDEO | 0.20-0.70 | 0.01-0.30 | 0.02-0.20 | 0.01-0.15 | 0.01-0.10 |
| Proprietates physicae | |||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
|
| 8.9 | - | 16-17.6 | 80 | 320 | |
| Proprietates mechanicæ | ||||
| Temperamentum | Dureza HV |
Testatio Tensionis | ||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
||
| R540 | 160-190 | 540-630 | ＞520 | ＞7 |
| TR08 | 150-180 | 520-620 | ＞500 | ＞7 |
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci sunt in stock. Aut infra 30 dies, si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, possumus praebere exemplar
Q: Quae sunt tua termini solvendi
A: 30% T/T ante propter praestationem, reliquum ante navationem. Et pretium dependet a materia et quantitate
Si habes alteram quaestionem, noli hesitare nobiscum conari.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN