C19000 Ligamentum introductio
Addendo Ni, P et alia elementa vestigialia ad matricem cupri, C19000 magnam vim, elasticitatem, praestantem conductivitatem, resistentiam relaxationi stress et resistentiad corrosioni stress exhibet. In terminis connector, formis lead frame, connectivis automobiliorum et aliis campis latissime utitur.
| Gradus | Compositio chymica (%)) ≤ | Crassitudo (mm) |
|||||
| GB | ASTM | EN | Cu | Ni | P | Zn | 0.08-5.0 |
| TNi1.1-0.25 | C19000 | CUNi1P | RESPONDEO | 0.9-1.3 | 0.15-0.35 | ＜0.8 | |
| Proprietates physicae | |||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10 -6\/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
|||
| 8.88 | 130 | 17.6 | 64 | 253 | |||
| Proprietates mechanicæ | Proprietates curvandi | ||||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R∕T(Crassitudo≤0.5mm) | ||||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Via mala | |||
| TM00 | 165-200 | 530-620 | 500-600 | ≥8 | 0.5 | 1.0 | |
| TM02 | 175-210 | 580-650 | 560-640 | ≥4 | 0.5 | 1.3 | |
| TM04 | 180-220 | 620-720 | 600-710 | ≥2 | 1.0 | 1.7 | |
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci sunt in stock. Aut infra 30 dies, si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, exemplum praebere possumus.
Q: Quae sunt tua condiciona praepositionis?
A: 30% T/T ante, reliquum ante navationem. Et pretium dependet a materia et quantitate.
Si habes alteram quaestionem, noli hesitare nobiscum conari.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN