Addendo Ni, Si, P et alias elementa parva ad fundamentum cuprum, C19010 magnam vim, elasticitatem, praestantem conductivitatem, resistentiam relaxationis stress et resistentiam corruptionis stress exhibet. In campo electrico applicatur, ut terminales conectorum, tabulae ductiles, connectores automotivorum, helices etc.
| Gradus | Compositio chemica (% ) ≤ | Crassitudo (mm) |
||||
| ASTM | Ni | Si | P | 0.08-5.0 | ||
| C19010 | 0.8-1.8 | 0.15-0.35 | 0.01-0.05 | |||
| Proprietates physicae | ||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
||
| 8.8 | 127 | 16.8 | 50 | 250 | ||
| Proprietates mechanicæ | Proprietates curvandi | |||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R\/T(Crassus＜0.8mm) | |||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Via mala | ||
| TM02 | 120-155 | 410-490 | ≥320 | ≥14 | 0.0 | 0.0 |
| TM03 | 140-165 | 460-520 | ≥340 | ≥12 | 0.0 | 0.0 |
| TM04 | 145-175 | 490-550 | ≥410 | ≥11 | 0.0 | 0.0 |
| TM06 | 150-180 | 520-590 | ≥440 | ≥9 | 0.5 | 0.5 |
| TM08 | 170-200 | 580-650 | ≥540 | ≥8 | 1.0 | 1.0 |
| TM10 | 180-220 | ≥620 | ≥580 | ≥5 | 1.5 | 1.5 |
| TM10S | ≥180 | ≥620 | ≥580 | ≥8 | 1.0 | 1.0 |