Addendo Sn, Ni, et alia parva elementa ad cuprum ut matrix, dat illud magnam vim, elasticitatem, et praestantem relaxationem stressis performance. Commune in lead frames, automobilium terminis, connectoribus etc. usus est.
| Gradus | Compositio chimica (% ) ≤ | Crassitudo (mm) |
|||||
| ASTM | Cu | Stannum | Ni | P | Zn | Other | 0.1-3.0 |
| C19040 | RESPONDEO | 1.0-2.0 | 0.7-0.9 | 0.02-0.09 | 0.01-0.3 | ≤1.0 | |
| Proprietates physicae | |||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
|||
| 8.9 | 130 | 17 | 30 | 140 | |||
| Proprietates mechanicæ | Proprietates flectendi | |||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R\/T (Crassitudo < 0.8mm) | |||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Mala via | ||
| H04 | 155-180 | 500-590 | 480-565 | ≥8 | 0 | 0.5 |