Addendo Zr et alia elementa vestigialia ad matricem cupream, exhibet alloy proprietates electrice egregias, conductivitatem thermicam, et flexionem formabilem. Est late usus in connectoribus magni currentis, tabulis leader, rectificatoribus, commutatoribus altius caloris, et componentibus diffusionis caloris.
| Gradus | Compositio chymica (%)) | Crassitudo (mm) |
|||
| GB | ASTM | EN | Cu | Zr | 0.08-3.0 |
| TZr0.1 | C15100 | CuZr0.1 | ≥99.8 | 0.05-0.15 | |
| Proprietates physicae | ||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
||
| 8.9 | 121 | 17.6 | 90 | 350 | ||
| Proprietates mechanicæ | Proprietates curvandi | |||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R\/T(Crassus＜0.8mm) | |||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Via mala | ||
| H01 | 80-110 | 280-320 | ≥180 | ≥22 | 0 | 0 |
| H02 | 90-120 | 300-360 | ≥240 | ≥15 | 0.5 | 0.5 |
| H03 | 100-130 | 330-390 | ≥310 | ≥8 | 1 | 1 |
| H04 | 110-140 | 370-430 | ≥350 | ≥4 | 1.5 | 1.5 |
| H06 | 120-150 | 410-460 | ≥395 | ≥2 | 2 | 2 |
| H08 | ≥140 | 440-500 | ≥420 | ≥1 | 2.5 | 2.5 |
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci sunt in stock. Aut infra 30 dies, si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, possumus praebere exemplar
Q: Quae sunt tua termini solvendi
A: 30% T/T ante propter praestationem, reliquum ante navationem. Et pretium dependet a materia et quantitate
Si habes alteram quaestionem, noli hesitare nobiscum conari.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN