C70350 latissime utitur in connectoribus electricis, semiconductorebus lead frames, terminis, etc. in systematibus tam signalis quam potentiae.
| Gradus | Compositio chimica (% ) ≤ | Crassitudo (mm) |
|||||
| ASTM | JIS | Cu | Ni | Si | Co | MG | 0.08-5.0 |
| C70350 | C7035 | RESPONDEO | 1.0-2.0 | 0.5-1.0 | 1.0-2.0 | ≤0.04 | |
| Proprietates physicae | |||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
|||
| 8.82 | 131 | - | 50 | 200 | |||
| Proprietates mechanicæ | Proprietates flectendi | |||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R⁄T( Crassitudo ＜0.8mm) | |||
| Robur Tensile Rm/Mpa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Mala via | ||
| TM02 | - | 690-830 | 675-780 | ≥5 | 1.0 | 1.5 |
| TM04 | 220-280 | 770-900 | 750-850 | ≥4 | 2.0 | 2.5 |
| TM06 | 240-300 | 840-970 | 810-920 | ≥1 | 2.5 | 2.5 |
QRA
Q: Quousque partus est tempus?
A: Commune re est intra 15 dies si merci sunt in stock. vel est minus quam 30 dies si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, possumus praebere exemplar
Q: Quae sunt tua termini praepositionis
A: 30% T/T ante, reliquum ante navationem. Et pretium dependet a materia et quantitate
Si habes alteram quaestionem, noli hesitare nobiscum conari.
Studio praxis in moderno consilio tendit, interiora landscapes ab inceptione nostra.
EN