Introducio C51900 Aerei Phosphori
C51900 est alligatio cupri stanni phosphori cum magna resistendo corruptioni, fatigationi, magneticitatibus, facile conflanda et optima performantia processionali. Hoc materialem late utitur in productione componentium elasticorum, partium durabilium et antimagneticarum in instrumentis et horologiis praecisionis. C51900 potest adhiberi ad producenda producta laminae phosphorus-cuprinae finissimae. Et C51900 (C5191/QSn6.5-0.1) cum successu mass-produxit producta hot-dip (physica electroplating) cum stratis stannum 1-6μm quod acceptabile est.
| Gradus | Compositio Chimica(%)≥ Microelementum(%)≤ | |||||||||||||||||
| Stannum | Al | Zn | Fe | Pb | Ni | P | Other | Cu | ||||||||||
| GB | QSn6.5-0.1 | 6.0-7.0 | 0.002 | 0.3 | 0.05 | 0.02 | 0.10-0.25 | 0.4 | RESPONDEO | |||||||||
| EN | CuSn6 | 5.5-7.0 | 0.2 | 0.1 | 0.02 | 0.2 | 0.01-0.4 | 0.2 | RESPONDEO | |||||||||
| ASTM | C51900 | 5.0-7.0 | - | 0.30 | 0.10 | 0.05 | - | 0.03-0.35 | - | RESPONDEO | ||||||||
| JIS | C5191 | 5.5-7.0 | - | 0.2 | 0.1 | 0.02 | - | 0.03-0.35 | 0.5 | RESPONDEO | ||||||||
| Proprietates physicae | ||||||||||||||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity (W∕(m·K)) |
||||||||||||||
| 8.86 | 118 | 17.2 | 13 | 75 | ||||||||||||||
| Gradus | status | Robur Tensile Rm\/MPa |
Tentio A11.3/% |
Dureza HV |
||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | EN | GB (HV) |
JIS (HV) |
ASTM (HR) |
EN (HV) |
| QSn6.5-0.1 | C5191 | C51900 | CuSn6 | O60 | O | O60 | R350/H080 | ≥315 | ≥315 | 330-435 | 350-420 | ≥40 | ≥42 | ≥45 | ≤120 | - | 18-66 | 80-110 |
| H01 | 1/4H | - | R420\/H125 | 390-510 | 390-510 | - | 420-520 | ≥35 | ≥35 | ≥17 | 110-155 | 100-160 | - | 125-165 | ||||
| H02 | 1/2H | H02 | R500\/H160 | 490-610 | 490-610 | 440-545 | 500-590 | ≥10 | ≥20 | ≥8 | 150-190 | 150-205 | 65-88 | 160-190 | ||||
| H04 | H | H04 | R560\/H180 | 590-690 | 590-685 | 550-680 | 560-650 | ≥8 | ≥8 | ≥5 | 180-230 | 180-230 | 86-95 | 180-210 | ||||
| H06 | EH | - | R640/H200 | 635-720 | 635-720 | - | 640-730 | ≥5 | ≥5 | ≥3 | 200-240 | 200-240 | - | 200-230 | ||||
| H08 | Sh | - | R720/H220 | ≥690 | ≥690 | - | ≥720 | - | - | - | ≥210 | ≥210 | - | ≥220 | ||||