Addendo Cr, Zr, et alia elementa vestigialia ad matricem cupri, C18140 praebet proprietates electrices, mechanicas, et thermicas egregias, necnon resistit molliori altis temperaturebus et relaxationi stressis.
Est in usu latissimo in terminis vehiculorum, laminis mobilibus relais, terminis PV, fusilibus, socketis, EV, HV terminis batteriarum, circuit breakeribus, et componentibus electricis et electronicis quae calorem generant ob minutiaturam.、
| Gradus | Compositio chemica (% ) ≤ | Crassitudo (mm) |
||||
| GB | ASTM | Cu | Cr | Zr | Si | |
| TCr0.3-0.15-0.03 | C18140 | RESPONDEO | 0.15-0.45 | 0.05-0.25 | 0.005-0.05 | 0.06-5.0 |
| Proprietates physicae | ||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity W(m·K) |
||
| 8.9 | 135 | 18.6 | 85 | 330 | ||
| Proprietates mechanicæ | Proprietates curvandi | |||||
| Temperamentum | Dureza HV |
Testatio Tensionis | 90°R\/T (Crassus＜0.5mm) | |||
| Robur Tensile Rm\/MPa |
Robur Renditionis MPa |
Tentio % |
Bonus modus | Via mala | ||
| R460 | 120-180 | 475-575 | 430-530 | ≥8 | 0 | 1 |
| R540 | 140-200 | 525-625 | 500-600 | ≥6 | 0 | 2 |
| R580 | 160-220 | 575-725 | 530-705 | ≥4 | - | - |
QRA
Q: Quousque partus est tempus?
A: Commune est intra 15 dies, si merci sunt in stock. Aut infra 30 dies, si merci non sunt in stock, est secundum quantitatem.
Q: Praebitisne exempla?
A: Ita, possumus praebere exemplar
Q: Quae sunt tua termini solvendi
A: 30% T/T ante propter praestationem, reliquum ante navationem. Et pretium dependet a materia et quantitate
Si habes alteram quaestionem, noli hesitare nobiscum conari.