Introducio C51900 Aerei Phosphori
C51900 est aes-stannum-phosphorus confectio cum alta resistendo corruptioni, fatigationi, magnetismo, facile brasando, et optima praeparatione operationis.
Hoc materialem late utitur in productione elasticorum membrorum, ferendarum et anti-magneticarum partium in instrumentis et horologiis praecisionis.
C51900 potest uti ad producendum phosphorus-cuprum lamina producta fine grano. Et C51900 (C5191/QSn6.5-0.1) cum successu mass-produxit producta hot-dip (physica electroplating) cum stratis stannum 1-6μm quod acceptabile est.
| Gradus | Compositio Chimica(%)≥ Microelementum(%)≤ | |||||||||||||||||
| Stannum | Al | Zn | Fe | Pb | Ni | P | Other | Cu | ||||||||||
| GB | QSn6.5-0.1 | 6.0-7.0 | 0.002 | 0.3 | 0.05 | 0.02 | 0.10-0.25 | 0.4 | RESPONDEO | |||||||||
| EN | CuSn6 | 5.5-7.0 | 0.2 | 0.1 | 0.02 | 0.2 | 0.01-0.4 | 0.2 | RESPONDEO | |||||||||
| ASTM | C51900 | 5.0-7.0 | - | 0.30 | 0.10 | 0.05 | - | 0.03-0.35 | - | RESPONDEO | ||||||||
| JIS | C5191 | 5.5-7.0 | - | 0.2 | 0.1 | 0.02 | - | 0.03-0.35 | 0.5 | RESPONDEO | ||||||||
| Proprietates physicae | ||||||||||||||||||
| Densitas (g/cm³) |
Modulus Elasticitatis (GPa) |
Coeficientis Expansionis Thermalis (×10-6/K) |
Conductivitas Electrifica (%IACS) |
Scelerisque Conductivity (W∕(m·K)) |
||||||||||||||
| 8.86 | 118 | 17.2 | 13 | 75 | ||||||||||||||
| Gradus | status | Robur Tensile Rm\/MPa |
Tentio A11.3/% |
Dureza HV |
||||||||||||||
| GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | ASTM | EN | GB | JIS | EN | GB (HV) |
JIS (HV) |
ASTM (HR) |
EN (HV) |
| QSn6.5-0.1 | C5191 | C51900 | CuSn6 | O60 | O | O60 | R350/H080 | ≥315 | ≥315 | 330-435 | 350-420 | ≥40 | ≥42 | ≥45 | ≤120 | - | 18-66 | 80-110 |
| H01 | 1/4H | - | R420\/H125 | 390-510 | 390-510 | - | 420-520 | ≥35 | ≥35 | ≥17 | 110-155 | 100-160 | - | 125-165 | ||||
| H02 | 1/2H | H02 | R500\/H160 | 490-610 | 490-610 | 440-545 | 500-590 | ≥10 | ≥20 | ≥8 | 150-190 | 150-205 | 65-88 | 160-190 | ||||
| H04 | H | H04 | R560\/H180 | 590-690 | 590-685 | 550-680 | 560-650 | ≥8 | ≥8 | ≥5 | 180-230 | 180-230 | 86-95 | 180-210 | ||||
| H06 | EH | - | R640/H200 | 635-720 | 635-720 | - | 640-730 | ≥5 | ≥5 | ≥3 | 200-240 | 200-240 | - | 200-230 | ||||
| H08 | Sh | - | R720/H220 | ≥690 | ≥690 | - | ≥720 | - | - | - | ≥210 | ≥210 | - | ≥220 | ||||